Improved hydrothermal-grown KTP crystal overcome the common electrochromicm damage of the flux-grown KTP, has high resistivity and high damage threshold. It is suitable for making electro-optic devices with excellent properties.
Advantages
- Low Insertion Loss
- Low half-wave voltage
- No-hygroscopic
- Wide optical bandwidth
- High laser induced damage threshold
- No piezoelectric ringing
- Thermally compensated design to operate on large temperate range
Applications
- Q-switching
- Pulse picking
- E-O Modulator
Specifications
| Transmission | > 98.5% @1064 nm |
| Aperture | From 2 mm × 2 mm to 10 mm ×10 mm |
| Electrical Resistivity | > 1011Ω•cm@25℃ |
| Extinction Ratio | > 20 dB@633 nm |
| AR Coatings | R < 0.2%@1064 nm |
| Damage threshold | 600 MW/cm2 at 1064 nm, for 10 ns pulses |
Model
| Voltage | λ/2 Voltage @1064 nm | ||
| Yype | X-Cut | Y-Cut | |
| Unit | V | V | Ohm.cm |
| 3*3*10mm(pairs) | 1200 | 1000 | >1011 |
| 4*4*10mm(pairs) | 1600 | 1300 | |
| 5*5*10mm(pairs) | 2000 | 1600 | |
| 6*6*10mm(pairs) | 2300 | 1900 | |
| 7*7*10mm(pairs) | 2700 | 2200 | |
| 8*8*10mm(pairs) | 3100 | 2500 | |
| 9*9*10mm(pairs) | 3500 | 2800 | |